Chongqing Xiangri Tu Medical, Fluke, Shenzhen Metrology Institute “2013 Fluke New Product Launch Conference
In September 2013, Ritu Technology Chongqing Branch called Shenzhen Ritu Medical Equipment Co., Ltd. to celebrate the 2013 Shenzhen Headquarters and the US Fluke, Shenzhen Metrology Institute and Shenzhen University. “2013 Fluke New Product Launch Conference and Shenzhen Metrology Institute Simulation The instrument calibration station seminar was successfully held. Product Description Engineering Plastics Products,Engineering Plastics,Engineered Plastics ZHENJIANG CHUNHUAN SEALING MATERIALS CO.,LTD(GROUP) , http://www.chsealing.com
In September 2013, Ritu Technology Chongqing Branch called Shenzhen Ritu Medical Equipment Co., Ltd. to celebrate the 2013 Shenzhen Headquarters and the US Fluke, Shenzhen Metrology Institute and Shenzhen University. “2013 Fluke New Product Launch Conference and Shenzhen Metrology Institute Simulation The instrument calibration station seminar was successfully held. According to the relevant media reports, the venue layout is only a strip, the product introduction and posters are carefully arranged by our staff, the atmosphere is warm and professional, on-site we show the full range of medical products from Fluke Fluke: Prosim3, Prosim4 Prosim8 Such as vital signs simulator, blood oxygen simulator, IDA5, VT305 and other airflow analyzers, ESA620, and other products. Products are widely used in the medical device manufacturing industry, covering the R & D department, production line, quality management department, after-sales service department, technical supervision organization (medical registration testing, measurement testing certification). At the same time, we also invite Shenzhen Institute of Metrology, Shenzhen University experts to do technical explanations, the client covers medical, electronic manufacturing and other industries, mainly representatives of Shenzhen Mindray, Philips, Koman medical equipment, Huateng Biological, Bao Laite medical Technology shares, China Inspection Group Southern electronic product testing and other corporate procurement engineer friends joined the site.
The daily medical marketing team presented the highest-end equipment for the technical engineers. The organizing committee specially prepared for this meeting for a long time. We invited Fluke Product Technology Manager and Cui Manager to do technical introduction and technical solutions for the customers. In an endless stream of consultations on various issues, Cui Manager also gave a very professional technical solution, left a deep impression on the field engineers, and carefully prepared a sumptuous dinner to thank Xiamen for supporting us all the time. friends.
Mr. Wang Wei, Manager of Chongqing, called the event organizing committee to congratulate the success of the event.
Http://news.chinawj.com.cn Submission:
PVDF rod with 20-150mm diameter
Description
PVDF has high strength, super chemical resistance, high temperature resistance, UV resistance. What's more, its dielectrical property is also very good. Compared with PTFE, it has higher surface hardness. The global production capacity of PVDF is only next to PTFE in the fluoropolymer family
Characteristics
-Excellent chemical resistance
-High toughness and rigidity
-Good dielectrical properties
-Good UV and radiation resistance
-Easy to machine
-Good sliding resistance,
-High wear resistance
-Nice dimensional stability
Applications
Silicon chip carrier
PVDF nozzle
Technical Data Sheet
PROPERTIES Test Method Unit Value
I.Physical Properties
Density ISO 1183 g/cm3 1.8
Water absorption 24hrs ISO 62 % <0.05
II.Thermal Properties
Heat deflection temperature - HDT/A ISO 75-2 ºC 104
Min. service temperature ºC -40
Max. service temperature-Long Term ºC 150
Thermal conductivity at 23 ºC DIN 11359 W/(K*m) 0.13
Coefficient of linear thermal expansion ISO 11359 10-4*K-1 0.2
Flammability Rating(6mm thickness) UL 94 - V-0
III.Mechanical Properties at 23ºC
Tensile strength at yield ISO 527-2 MPa 50
Tensile strength at break ISO 527-2 Mpa 46
Elongation at break ISO 527-2 % ≥50
Modulus of elasticity after tensile test ISO 527-2 MPa 2,000
Modulus of elasticity after flexural test ISO 178 MPa 2,000
Hardness - Shore D DIN 53505 78
Charpy impact strength ISO 179 kJ/m2 N. B.
Friction coefficient DIN 53375 0.33
IV.Electrical Properties at 23ºC
Dielectric constant at 1 MHz IEC 60250 106Hz 7.25
Dielectric loss factor at 1 MHz IEC 60250 106Hz 0.18
Volume resistively IEC 60093 Ohm (Ω) * cm ≥1013
Surface resisively IEC 60093 Ohm (Ω) ≥1014
Dielectric strength IEC 60243-1 kV/mm 22
NOTE: 1 g/cm3 = 1,000 kg/m3, 1 Mpa = 1 N/mm2, 1kV/mm = 1 MV/m
Statement:
Property data contained herein are typical values of resin for your reference and comparison purposes only. PRIOR will not provide any legally binding guarantee of certain properties, or any suitability.