What are the main points of PVC cable compound formula design?
Non-Nitrosamines Rubber Accelerators are environmental-friendly, which normally includes products, like CaO-80GE F200, CBS-80GE F140, MBT-80GE F140, MBTS-75GE F140, OBSH-75GE, S-80GE F200, TBBS-75GE F200, TBzTD-70GE F140, ZBEC-70GE F140, ZDTP-50GE F500, ZDT-50GE F500, ZBOP-50GE F140, TP-50GE F140, ZBPD-50GE F140, ZnO-80GE F140, EG3A-75GE F140, LHG-80GE F140, Retarder E-80GE , CLD-80GE F500 and MTT-80GE F500. Non-Nitrosamines Rubber Accelerator Non-Nitrosamines, Nitrosamines-Free, Rubber Chemicals, Rubber Chemicals Ningbo Actmix Rubber Chemicals Co.,Ltd. (Ningbo Actmix Polymer Co.,Ltd.) , http://www.actmix-chemicals.com
(2) For general insulation grade cable material, plasticizer dosage is 40~50PHR. Stabilizer 6 ~ 8PHR. Lubricant l ~ 1.5PHR. Filler l0PHR around; plasticizers, lubricants reference jacket grade cable material;
(3) Plasticizers such as DBP with high volatility cannot be used for cable materials;
(4) In addition to high temperature resistant cable materials, high temperature plasticizers should be used. Stabilizer dosage should also be increased. Add 0.3 to 0.5 PHR of antioxidant;
(5) For cable materials with high insulation requirements. Calcined clays should be used as fillers (plasticizing efficiency of polymeric polymeric plasticizers is poor. The amount of plasticizer should be increased as appropriate when formulating formulations;
(7) When formulating a transparent cable formulation. Should be selected and the resin compatibility good saggers. Direct use of organic tin and other transparent stabilizers, and strictly control the amount of lubricant added;
(8) Design of flame retardant cable compound Should use a composite flame retardant system is appropriate;
(9) When formulating a high degree of polymerization cable formulation. Should use a composite processing modifier to improve its processing performance;
(10) When formulating non-migratory cable compounds, polyester or high polymer plasticizers should be selected;
(11) When the compound stabilizer is used, its amount is slightly more than that of the three salt stabilizers;
(12) Under the condition that the cable material is processed and used normally. To minimize the amount of stabilizer. Prevent excessive amounts of it from producing a "filler effect."
Cable material production process (1) Single screw extruder production process:
Raw materials --- ingredients --- high-speed kneading machine --- single-screw extruder --- air-cooled --- screening magnetic separation --- measurement --- packaging.
(2) single screw two-stage extruder production process:
Raw materials --- ingredients --- high-speed kneading machine --- single-screw double-stage granulator --- cooling and drying --- screening magnetic separation --- measurement --- packaging.
(3) Twin-screw extruder production process:
Raw materials --- ingredients --- high-speed kneading machine --- twin-screw extruder --- air-cooled --- screening magnetic separation --- measurement --- packaging.
(4) Rolling granulation production process flow:
Raw materials----Advanced--High-speed kneader--Intermixer--Two-roll mill--Cooling sink--Drying--Cutter--Selecting magnetic separation-- - Metering - Packaging.