Transport Package: Wooden Pallet /Plywood Pallet /Steel Frame Pallet
Specification: SGS, ROHS
Origin: China
HS Code: 760612
Model NO.: 5754
Alloy: Alloy
Sample: Free
Type: Aluminum Sheets
Shape: Flat
Trademark: Baodi
Transport Package: Wooden Pallet /Plywood Pallet /Steel Frame Pallet
Specification: SGS, ROHS
Origin: China
HS Code: 760612
Alloy: 5754
Temper: H14, H22, H24, H18, H26, H16, H32, H34, O
Thickness(mm): 0.25-300
Width(mm): 600-2200
Length(mm): 1000-6000
Packing: Wooden/veneer pallet, wooden/veneer case
Unit Price/Payment: FOB, CIF, CFR
HS Code: 7606125900
MOQ: 2.0-2.5MT/Size
Chemical composition: Aluminum Balance Chromium 0.1-0.6 Copper 0.1 max Iron 0.4max Magnesium 2.6-3.6 Manganese 0.5 Remainder Each 0.05 max Remainder Total 0.15 max Silicon 0.4 max Titanium 0.15 max Zinc 0.2 max
Characteristic: Anti-rust material, anti-corrosion, good welding, easy to be shaped, anodized. Suitable for deep drawing. Application: 5754 aluminum is widely used in car, ships, liquid tank, oil tank, components of car, rivet.
Brief introduction: 1. 20 years' experance in aluminum area 2. ISO 9001 Certificated 3. Have present stock for standard size 4. Small quantity is acceptable 5. 100% brand new 6. Surface: Flat, smooth, bright, no rolling mark, no black spot, no scratch Â
Specification
Name: 5000 series Aluminum Sheet
Alloy: 5052, 5005, 5754, 5083 etc.
Temper: O, H12, H22, H32, H14, H24, H26, H18, H112 etc.
Thickness: 0.2-200mm
Width: Up to 1800mm
Length: up to 6000mm
Surface treatment: mill finished, PVC coated, Print marks
Feature
Machinability: It has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry.
Forming: It is readily formed at room temperature. Successive cold working decreases the formability.
Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold working.
Forging: It may be forged in the temperature range of 950 FÂ down to 500 F
Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary.
Annealing: Anneal at 650 FÂ and air cool.
Hardening: Hardens only from cold working.
Application
hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc.
Alloy
Chemical Component %≤
Si
Fe
Cu
Mn
Mg
Cr
Ni
Zn
Ti
others
Al
single
total
5052
0.25
0.4
0.1
0.1
2.2-2.8
0.15-0.3
\
0.1
\
0.05
0.15
remainder
5005
0.3
0.7
0.2
0.2
0.5-1.1
0.1
\
0.25
\
0.05
0.15
remainder
5754
0.4
0.4
0.1
0.5
2.6-3.6
0.3
\
0.2
0.15
0.05
0.15
remainder
5083
0.4
0.4
0.1
0.4-1.0
4.0-4.9
0.05-0.25
\
0.25
0.15
0.05
0.15
remainder
Contact
Ms. Margaret
Â
Tel: 0086-15553544561
Alloy: 5754
Temper: H14, H22, H24, H18, H26, H16, H32, H34, O
Thickness(mm): 0.25-300
Width(mm): 600-2200
Length(mm): 1000-6000
Packing: Wooden/veneer pallet, wooden/veneer case
Unit Price/Payment: FOB, CIF, CFR
HS Code: 7606125900
MOQ: 2.0-2.5MT/Size
Chemical composition: Aluminum Balance Chromium 0.1-0.6 Copper 0.1 max Iron 0.4max Magnesium 2.6-3.6 Manganese 0.5 Remainder Each 0.05 max Remainder Total 0.15 max Silicon 0.4 max Titanium 0.15 max Zinc 0.2 max
Characteristic: Anti-rust material, anti-corrosion, good welding, easy to be shaped, anodized. Suitable for deep drawing. Application: 5754 aluminum is widely used in car, ships, liquid tank, oil tank, components of car, rivet.
Brief introduction: 1. 20 years' experance in aluminum area 2. ISO 9001 Certificated 3. Have present stock for standard size 4. Small quantity is acceptable 5. 100% brand new 6. Surface: Flat, smooth, bright, no rolling mark, no black spot, no scratch Â
Specification
Name: 5000 series Aluminum Sheet
Alloy: 5052, 5005, 5754, 5083 etc.
Temper: O, H12, H22, H32, H14, H24, H26, H18, H112 etc.
Thickness: 0.2-200mm
Width: Up to 1800mm
Length: up to 6000mm
Surface treatment: mill finished, PVC coated, Print marks
Feature
Machinability: It has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry.
Forming: It is readily formed at room temperature. Successive cold working decreases the formability.
Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold working.
Forging: It may be forged in the temperature range of 950 FÂ down to 500 F
Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary.
Annealing: Anneal at 650 FÂ and air cool.
Hardening: Hardens only from cold working.
Application
hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc.